Re: Very Large Hull Indentation
I seem to recall reading this is fairly common on some lighter weight hulls. Most solids are not really solids, the resins in glassfibre qualify and will creep slowly over time.
I also agree that this does not look bad. As long as the glass is not cracked or spiderwebbing, I would not worry too much about it