SailNet Community - Reply to Topic
Thread: Rubber = Galvanic Corrosion? Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :
Post Icons
You may choose an icon for your message from the following list:

Register Now

In order to be able to post messages on the SailNet Community forums, you must first register.
Please enter your desired user name, your email address and other required details in the form below.
Please note: After entering 3 characters a list of Usernames already in use will appear and the list will disappear once a valid Username is entered.

User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.


Confirm Password:
Email Address
Please enter a valid email address for yourself.

Email Address:


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

  Additional Options
Miscellaneous Options

Click here to view the posting rules you are bound to when clicking the
'Submit Reply' button below

  Topic Review (Newest First)
02-09-2008 07:50 PM
Rockter Rubber will not conduct electrickery.
You might see corrosion underneath it where it has been excluding oxygen from stainless, for example, but the idea that it would take part in a corrosion reaction sounds very questionable.
02-09-2008 04:31 PM
Sasha_V I use PET plastic... Works like Mylar, but is free and always close to hand (drink bottle material).
02-09-2008 02:38 PM
Valiente See? Mylar sheets...something new I've learned today. I suppose you could cut up a blown-out composite sail as well!
02-09-2008 08:51 AM
thekeip Instead of rubber, I commonly use Mylar, available in sheets of various thicknesses, at art supply stores. Five-mil (0.005") drafting Mylar is an extremely tough material and easy to cut and use.
Howard Keiper
Sea Quest
02-09-2008 06:48 AM
hphoen Carbon conducts electricity, true, but that has nothing to do with corrosion. The material has to be capable of participating in an electrolyitic reaction, i.e, giving up or receiving electrons from another substance., usually in the presence of water. I've never heard of elemental carbon being involved in an electrolytic reaction. It reacts, of course, but needs heat and an oxidixzer to get started (combustion).

If salt water gets trapped between rubber and an aluminum tank, you could get corrosion, but the only role the rubber would play would be holding the water on the surface of the tank.
02-09-2008 06:21 AM
Sasha_V It depends on the ruber. Vulcanised rubber would have the most activated carbon in it...but you would not use it for much boat related stuff anyway...

latex rubber is safe, as is silicone "rubber" and any number of rubbers that have achieved the same stability as vulkcanised rubber, but through chemical processes instead of heat.

All in all, I think you are safe. really.
02-09-2008 06:16 AM
billangiep I think the more likely event would be moisture being trapped between the rubber and the aluminum tank causing the corrosion.
02-09-2008 03:50 AM
KeelHaulin Could you post the link to that website that talks about it? I can't say unless I have read that article. Normally rubber is an excellent electrical insulator; and as such it would help prevent electrical current between dis-similar metals. If it is a specific type of rubber that they are concerned with it might be the reason for the recall.

Carbon exists in many, many non-conductive things; it is the type of carbon bonds (at the molecular level) that would determine it's conductivity. CF probably has some conductive properties; but you would have to be attached to the roving directly because the plastic that encases it is non-conductive.
02-09-2008 02:26 AM
Originally Posted by sailboy21 View Post
While browsing the web for boat stuff (what else?) I ran across a fuel tank manufacturer that issued a warning not to use rubber in contact with aluminum. The reason stated, was rubber contains carbon which exists on the galvanic series, and is slightly more noble than passivated stainless steel.
I immediately thought of my stainless steel masthound for my inner forestay.
I had placed a rubber gasket to insulate the stainless from the aluminum. It had never occurred to me that I may have been creating a bigger galvanic cell! I removed the masthound and found zero evidence of corrosion after two years.
Has anyone heard of an issue with rubber against aluminum? I usually use HDPE as an insulating material, and religiously use tefgel on fasteners, but I had a sheet of generic black rubber gasket material handy at the time. Should I replace the rubber with a sheet of HDPE or leave it alone?
Certain rubber gaskets and shrouds do contain carbon... Carbon is actually a very good electrical conductor (Carbon Fiber for example is a great electrical conducer)..

So the marks are not that far off - you can minimize the effect / severely limit however... if you are attaching to another metal - lubricate it with silicon sealant which is not as conducive and will prevent contact of the two...If the boundary is there - due to the lower level in the rubber - you will be out of harms way....but it is not a myth it actually happens...
02-09-2008 01:08 AM
Valiente I'll try to check this out in my Metal Corrosion on Boats book. I hope it's false, as I use rubber sheeting for this purpose in a few spots as well.
This thread has more than 10 replies. Click here to review the whole thread.

Posting Rules  
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

For the best viewing experience please update your browser to Google Chrome