SailNet Community - Reply to Topic

   Search Sailnet:

 forums  store  


Quick Menu
Forums           
Articles          
Galleries        
Boat Reviews  
Classifieds     
Search SailNet 
Boat Search (new)

Shop the
SailNet Store
Anchor Locker
Boatbuilding & Repair
Charts
Clothing
Electrical
Electronics
Engine
Hatches and Portlights
Interior And Galley
Maintenance
Marine Electronics
Navigation
Other Items
Plumbing and Pumps
Rigging
Safety
Sailing Hardware
Trailer & Watersports
Clearance Items

Advertise Here






Go Back   SailNet Community > On Board > Gear & Maintenance > Re-Chroming Lewmar Winches
 Not a Member? 


Thread: Re-Chroming Lewmar Winches Reply to Thread
Title:
  

By choosing to post the reply below you agree to the rules you agreed to when joining Sailnet.
Click Here to view those rules.

Message:
Trackback:
Send Trackbacks to (Separate multiple URLs with spaces) :
Post Icons
You may choose an icon for your message from the following list:
 

Register Now

In order to be able to post messages on the SailNet Community forums, you must first register.
Please enter your desired user name, your email address and other required details in the form below.
Please note: After entering 3 characters a list of Usernames already in use will appear and the list will disappear once a valid Username is entered.
User Name:
Password
Please enter a password for your user account. Note that passwords are case-sensitive.
Password:
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:

Log-in

Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.



Click here to view the posting rules you are bound to when clicking the
'Submit Reply' button below


Additional Options
Miscellaneous Options

Click here to view the posting rules you are bound to when clicking the
'Submit Reply' button below


Topic Review (Newest First)
12-17-2009 06:01 PM
botanybay
Quote:
Originally Posted by arf145 View Post
That's usually Previous Owner
Ah, much like my "Came With The Boat"

Thanks
12-17-2009 03:41 PM
arf145
Quote:
Originally Posted by botanybay View Post
What is "by the PO" I assume that was the vendor you used?
That's usually Previous Owner
12-17-2009 02:05 PM
botanybay
Quote:
Originally Posted by gtod25 View Post
I have 6 of these re chromed by the PO (2 x 28 ST, 1 x 22 ST, 1 x 22, and 2 x 16 - all Barlow) and had no idea about the technology. I am still a little concerned about the "grip" but they look nice. Time will tell.

They definitely look great!

What is "by the PO" I assume that was the vendor you used?

Thanks
12-17-2009 01:25 PM
gtod25
Thanks for all the great info....

I have 6 of these re chromed by the PO (2 x 28 ST, 1 x 22 ST, 1 x 22, and 2 x 16 - all Barlow) and had no idea about the technology. I am still a little concerned about the "grip" but they look nice. Time will tell.

12-17-2009 12:58 PM
botanybay
Quote:
Originally Posted by dillybar View Post
Gramp34 has it exactly right. The main difference between the two is the prep and process. Decorative chrome uses some brightening alloys and is designed to throw well into nooks and crannies in very thin layers where industrial chrome is engineered for hardness, and speed of deposition but the material is similar.
Decorative chrome typically uses a copper layer first primarily to seal the parent material for corrosion resistance as plated chrome is very porous. That is not to say industrial chrome can not be plated over copper,(it's done all the time for carbon steel marine duty piston rods) it's just that industrial applications don't normally require it so industrial shops have no need to dedicate space and expense to have a copper tank.

Ind. chrome can easily be deposited in thicknesses exceeding .020",however .002" would be lots for a winch that combined with the harder deposit (78 RC) means much greater wear resistance. Because mirror finishes are not required, Ind. shops won't have the buffing equipment to get a show finish, again, not to say ind. chrome can't buff up surprisingly well.

So what it boils down to is what your priorities are - Dec. chrome will look fantastic, wear reasonably well and protect the base material well whereas heavily plated ind. chrome over copper will last for the life of the boat and if reverse etched for 30 sec. after plating will grip your lines like sh*t to a blanket but will have a grey appearance. BTW you would expect to pay 2 to 3 times more for the industrial chrome proces described.

And yes, I did stay at a Holiday Inn Express last night (and own an industrial chrome shop).
Thank you so much for the information!

I obtained a reference to what is originally on the Winches which I am still trying to work through completely but it is a copper undercoat, a double or triple laer of nickel to a total of 25 microns, and then a minimum of 0.5 microns of chromium.

The parts are copper plated, polished, and then re-coppered and polished prior to the three coats of nickel and then a chromium layer.

At least I now know what I am trying to achieve!

The base specification is BS EN 12540:2000 service condition 4.

Off to find a shop which can do this!

I'll let you know what I find.
12-17-2009 02:33 AM
SVPrairieRose
Quote:
Originally Posted by Jeff_H View Post

As to the winches on my current boat, while this surface has been polished back to bronze, I have not rechromed it. I see boats as tools to me and see this as a wear pattern of a well used fine tool.

Jeff
Cheers to that!
12-17-2009 12:15 AM
dillybar Gramp34 has it exactly right. The main difference between the two is the prep and process. Decorative chrome uses some brightening alloys and is designed to throw well into nooks and crannies in very thin layers where industrial chrome is engineered for hardness, and speed of deposition but the material is similar.
Decorative chrome typically uses a copper layer first primarily to seal the parent material for corrosion resistance as plated chrome is very porous. That is not to say industrial chrome can not be plated over copper,(it's done all the time for carbon steel marine duty piston rods) it's just that industrial applications don't normally require it so industrial shops have no need to dedicate space and expense to have a copper tank.

Ind. chrome can easily be deposited in thicknesses exceeding .020",however .002" would be lots for a winch that combined with the harder deposit (78 RC) means much greater wear resistance. Because mirror finishes are not required, Ind. shops won't have the buffing equipment to get a show finish, again, not to say ind. chrome can't buff up surprisingly well.

So what it boils down to is what your priorities are - Dec. chrome will look fantastic, wear reasonably well and protect the base material well whereas heavily plated ind. chrome over copper will last for the life of the boat and if reverse etched for 30 sec. after plating will grip your lines like sh*t to a blanket but will have a grey appearance. BTW you would expect to pay 2 to 3 times more for the industrial chrome proces described.

And yes, I did stay at a Holiday Inn Express last night (and own an industrial chrome shop).
12-16-2009 10:29 PM
CLucas
Quote:
Originally Posted by botanybay View Post
Do you know what process they used? i.e. hard chrome vs. show chrome? The $150/winch is very reasonable I am trying to determine what it is I should ask for. If you have gotten a couple of years out of them and they still look good this is definitely on the right path!

As best I can tell, the hard chrome is a thick coating applied directly to the base metal and will have some degree of imperfections, the show chrome uses a base coat of copper which is buffed to a high polish and then a layer of nickle is applied and buffed to a high polish prior to the final layer of chromium.

I am guessing that the hard chrome (also known as "industrial chrome") which is used to build up crankshaft diameters and then milled or for hydraulic cylinders is probably what I am looking for.

Even if I had to re-chrome every few years that would be good.

Thank you so much for the feedback that this is possible and the results can be good.
Not sure of the process they used, but I will tell you that it has held up nicely. I may be at the boat this weekend and will take some photos. As other have reported, the drums seemed to lose some of their grip, but I also replaced my running rigging the same year and was attributing some of that to the new sheets. Not sure whether it's improved as the sheets have broken in or if I've just gotten used to it.
12-16-2009 07:22 PM
botanybay
New England Chrome looks promising!

Quote:
Originally Posted by Gramp34 View Post
I'd be careful specifying hard chrome for winches. It doesn't provide particularly good corrosion protection to the base metal.

Hard chrome is what's used on the piston rods of hydraulic cylinders. It's actually fairly porous, and holds a film of oil in it. If you see a cylinder that's been exposed to the weather for a few months without cycling, you'll see rust coming though. I expect salt exposure would accelerate that process.

On "decorative" chrome the nickel layer provides most of the corrosion protection. The final chrome layer protects the nickel from tarnishing.

A shop doing decorative work can give you a thicker layer of chrome. They just leave the parts in the tank longer. Tell them the winch drums need to be particularly wear resistant and they can probably recommend settings for them.

New England Chrome has been advertising in Good Old Boat for years. I don't have any experience with them, but they might be worth a call.

Good luck,

Tim
Thank you for the lead on new england chrome, this is the first place I have seen specifically note that they do winch drums for sailboats.

I really hate to tell someone what they should be using but rather have someone with experience tell me what they think I should be doing. I will give them a call tomorrow morning and see what they can tell me.

David
12-16-2009 07:01 PM
Jeff_H The pattern of premature wear on the smooth top of the base of the winch drum almost happens by design. Winches need to be located so that the lead of the line drags acrous this surface in order to prevent over-rides of the line. Since the line is at its greatest tension and its dragging across this surface rather than sliding under control, this is where wear should be expected.

As to the winches on my current boat, while this surface has been polished back to bronze, I have not rechromed it. I see boats as tools to me and see this as a wear pattern of a well used fine tool.

Jeff
This thread has more than 10 replies. Click here to review the whole thread.

 
Posting Rules
You may post new threads
You may post replies
You may post attachments
You may edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On


All times are GMT -4. The time now is 12:42 AM.

Add to My Yahoo!         
Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2014, vBulletin Solutions, Inc.
SEO by vBSEO 3.6.1
(c) Marine.com LLC 2000-2012

The SailNet.com store is owned and operated by a company independent of the SailNet.com forum. You are now leaving the SailNet forum. Click OK to continue or Cancel to return to the SailNet forum.