SailNet Community - Reply to Topic
Thread: 25 foot trailer yacht - Rudder Questions Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :
Post Icons
You may choose an icon for your message from the following list:

Register Now

In order to be able to post messages on the SailNet Community forums, you must first register.
Please enter your desired user name, your email address and other required details in the form below.
Please note: After entering 3 characters a list of Usernames already in use will appear and the list will disappear once a valid Username is entered.

User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.


Confirm Password:
Email Address
Please enter a valid email address for yourself.

Email Address:


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

  Additional Options
Miscellaneous Options

Click here to view the posting rules you are bound to when clicking the
'Submit Reply' button below

  Topic Review (Newest First)
02-02-2010 04:31 PM
landmarine thanks for your prompt reply. As we are racers we wanted the extra buoyancy in the stern - The rudder is a swinging one located in a box - I calculate when fully immersed in seawater the buoyancy will be around 7.5kg - we reckon we can hold it down with the tie-down rope (multi-purchase if need be). Thanks for the good advice
02-02-2010 04:21 PM
sailingdog What weight is the green code Divinylcell foam. I'd point out that you may want to weight the rudder so that it is neutrally buoyant or a bit heavier than that it doesn't tend to float up.

I wouldn't use uni-glass in this application, since the loads are going to be multidirectional. Triaxial roving would be a good material to use...with some regular cloth or CSM over it to protect it from the fairing/sanding process.

I'd also recommend putting in a layer or two of kevlar, preferably under CSM/cloth but over the triaxial roving. The reason I'd add the kevlar is that it is highly abrasion and puncture resistant.

I wouldn't use Carbon fiber in a rudder, since the carbon fiber can cause galvanic issues with metal hardware, which the fiberglass and kevlar will not.

Hope that helps.
02-02-2010 04:00 PM
25 foot trailer yacht - Rudder Questions

I have a GRP 25 foot trailer yacht that I'm wanting to improve the rudder on. Basically the foam GRP one I have weighs almost 10kg and is not optimised in shape and its leading edge is 40mm aft of the gudgeon pivot line - It feels like I'm dragging 2 buffalos!!

I intend to construct a new one out of Divinycell (HD) / e-glass / epoxy resin (resin infusion) - and wanted a few tips if possible on the following subjects?:

1) Is the green code Divinycell suitable? blade is approx 1300mm x 360mm - and will need two 20mm thick sheets laminated together with e-glass in between for datum line and strength at the edges
2) What would you recommend in terms of laminate cloths? Someone suggested two layers of uni-glass or carbon followed by a single tri-axial sheet??
3) What additional thickness allowance do I need to make for the 3? skins (what cloth weight should I use)
4) I'm getting assistance from a boat builder but just wanted a 2nd opinion on things - The trailing edge is the difficult one as we need to have a thickness of no more than 1-2mm here. We are using a modified NACA 0012 section with hollowed out trailing edges (concave on exit straights)
5) any other pointers you think might be helpful please??

Any assistance appreciated thanks

Posting Rules  
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

For the best viewing experience please update your browser to Google Chrome