SailNet Community - Reply to Topic
Thread: Sabre 38 core moisture Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :
Post Icons
You may choose an icon for your message from the following list:

Register Now

In order to be able to post messages on the SailNet Community forums, you must first register.
Please enter your desired user name, your email address and other required details in the form below.
Please note: After entering 3 characters a list of Usernames already in use will appear and the list will disappear once a valid Username is entered.

User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.


Confirm Password:
Email Address
Please enter a valid email address for yourself.

Email Address:


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

  Additional Options
Miscellaneous Options

Click here to view the posting rules you are bound to when clicking the
'Submit Reply' button below

  Topic Review (Newest First)
03-24-2011 11:47 AM
turbulicity Keep in mind that the moisture readings are not always reliable. Especially below the water line. You could check the condition of the core by drilling the inner layer glass and core. But then, if the hull sounding was OK, you are probably good to go. Make sure you follow the previous recommendations and reseal the thru-hulls.

Congrats on your new boat.
03-24-2011 10:50 AM
Andrewbradley Thanks guys,

I have just spoke with the surveyor and he has said that the problems are so minor that they are not worth worrying about. The outer laminate is thicker than most single skin glass vessels.He also stated that it was built far better than many European boats and that if all cored construction was carried out to this standard there would never be any bad rep with cored hulls! Decision made.

Thanks again, Andrew.
03-22-2011 02:49 AM
celenoglu I totally agree with the surveyor. The problems are minor and can be repaired easily. 11% is really a good reading. 18% is high but not too much. Being around the thru hulls indicates water ingress around the thru hulls. Removing and repairing these areas with epoxy will overcome this problem.
03-21-2011 11:11 PM
mitiempo If a cored hull is properly constructed and the core is removed in the areas of through hulls and replaced with thickened epoxy there should not be a problem. The big issue with cored decks is the dozens of ways water can get in, especially after years needing the hardware rebedded and it not being done.

The hull will be solid glass in the keel area and the shaft log and rudder areas. The total number of ways for water to enter, except after a collision, are about 7 through hulls. It they are pulled, core removed around them, and replaced with thickened epoxy there should be no issues.
03-21-2011 08:33 PM
t22cayuga I'd be inclined to trust the surveyor's opinion on this, he's the expert you hired who actually examined the boat. I personally wouldn't be scared off by what you've described as pretty minor moisture issues.
03-21-2011 12:18 PM
Yorksailor I have a 26 yr-old balsa cored deck and that made me nervous, I have seen many boats with deck soft spots, until we drilled 2 inch cores and found it sound during the renovation of the teak.

I would never buy a cored hull...just too much potential for problems...The following article details them.

Cored Hull Bottoms

Good luck Phil
03-21-2011 12:03 PM
Sabre 38 core moisture

Hi All,

Just had a 1989 Sabre 38 mkll surveyed which has a fully cored hull and deck.
Surveyor has indicated all moisture readings around hull are 11% and should be considered dry...Except in a couple of places around thru'hulls below the waterline where moisture redings are 18%. Vessel has been on hard since October.
Another couple of similar areas are found on the coachroof around organiser and on the fordeck in a line running between the two forward cleats.
Again, no delamination just localised elevated moisture readings.
The surveyor is indicating that this is normal for a vessel of this age and nothing to be alarmed at and the hull issues can be cured by removing thru hull fittings and scraping core back, filling with epoxy then replacing fittings.
All was good but now am getting nervous of cored hulls. I know Sabre are a quality builder, the reason I chose in the first place, but would appreciate any views in particular from anyone who has had similar issues.
Thanks, Andrew.

Posting Rules  
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

For the best viewing experience please update your browser to Google Chrome